Hot Dip Galvanized Steel Stranded Wire Guy Wire
1. Raw material
A. wire rod: SAE1006-1082, including low-, mid- and high-carbon.
B. Zinc with 99.995% purity
2. Tensile strength range
Low carbon 1.6-8.0mm: 350-800mpa
High carbon 1.6-5.0mm: 900-1870mpa
3. Zinc coating
Class A, Class B and Class C, from 200g/m2 to 924g/m2
4. Application
Gabion mesh, Wiremesh, artware, metal hose, agriculture, binding for constrction
steel core wire for ACSR,Power cable,Overhead conductors,
Telecommunication cable,Messenger wire,Earth wire,Stay wire,Guy wire,Fence etc.
Features:
1. Very good anti-rusty ability
2. Good Wrap test result
3. Supersonic cleaning, Hcl cleaning- excellent cleaning.
4. High capacity- over 1500tons/month for this product
Technical Data:
1. Raw material
A. wire rod: SAE1006-1082, including low-, mid- and high-carbon.
B. Zinc with 99.995% purity
2. Tensile strength range
Low carbon 1.6-8.0mm: 350-800mpa
High carbon 1.6-5.0mm: 900-1870mpa
3. Zinc coating
Class A, Class B and Class C, from 200g/m2 to 924g/m2
4. Application
Gabion mesh, Wiremesh, artware, metal hose, agriculture, binding for constrction
steel core wire for ACSR,Power cable,Overhead conductors,
Telecommunication cable,Messenger wire,Earth wire,Stay wire,Guy wire,Fence etc.
Features:
1. Very good anti-rusty ability
2. Good Wrap test result
3. Supersonic cleaning, Hcl cleaning- excellent cleaning.
4. High capacity- over 1500tons/month for this product
Technical Data:
| Grade | Nominal Diameter of Strand | Tolerance of Diameter | Minimum Breaking Strength of Strand | Minimum Load at 1% Extension | Minimum Elongation | Nominal Area of Strand | Nominal Weight of Strand (approx) | Maximum Relaxation Loss after 1000 hours | |
| (Yield Strength) | (Gauge Length 610mm/24inch min) | Initial Load | Initial Load | ||||||
| 0.7 | 0.8 | ||||||||
| Ksi | mm | mm | KN | KN | % | mm2 | kg/1000m | % | |
| (Mpa) | (in) | (in) | (lbf) | (lbf) | (in2) | (lb/1000ft) | |||
| 250 | 9.53 | +/-0.40 | 89 | 80.1 | 3.5 | 51.61 | 405 | 2.5 | 3.5 |
| (1725) | (3/8 - 0.375) | (+/-0.016) | -20000 | -18000 | -0.08 | -272 | |||
| 11.11 | 120.1 | 108.1 | 69.68 | 548 | |||||
| (7/16 - 0.438) | -27000 | -24300 | -0.108 | -367 | |||||
| 12.70 | 160.1 | 144.1 | 92.9 | 730 | |||||
| (1/2 - 0.500) | -36000 | -32400 | -0.144 | -490 | |||||
| 15.24 | 240.2 | 216.2 | 139.35 | 1094 | |||||
| (6/10 - 0.600) | -54000 | -48600 | -0.216 | -737 | |||||
| 270 | 9.53 | -4.333333333 | 102.3 | 92.1 | 3.5 | 54.84 | 432 | 2.5 | 3.5 |
| -1860 | (3/8 - 0.375) | (+0.026/-0.006) | -23000 | -20700 | -0.085 | -290 | |||
| 11.11 | 137.9 | 124.1 | 74.19 | 582 | |||||
| (7/16 - 0.438) | -31000 | -27900 | -0.115 | -390 | |||||
| 12.70 | 183.7 | 165.3 | 98.71 | 775 | |||||
| (1/2 - 0.500) | -41300 | -37170 | -0.153 | -520 | |||||
| 15.24 | 260.7 | 234.6 | |||||||
| (0.6 - 0.600) | -58600 | -52740 |